Basic Formula for Plastic Reinforced Modification

Generally, there are plenty of plastic modifications, mainly including:

  • Reinforced modification: fiber reinforce,self-reinforce, molecular reinforce.
  • Filler Modifcation: Talc filler, CaCo3 filler, Kaolin filler,TiO2 filler, SiO2 filler, etc
  • Compounding & plastic alloy: PC+ABS, PET+PBT,etc
  • Flame retardant
  • Nano composite
  • Plastics grafting
  • Anti-aging modifcation
  • Functioning modification
  • Thermoplastics modification

The followings are some typical basic formulas for the plastic reinforce modifications

High Performance Fiber Glass Reinforcement PP

Homo-PP F40154%
GF30%
Coupling agent K-5500.5%
PP-g-MAH5%
POE-g-MAH10%
Lubricant0.5%

Processing Condition:

Compounding temperature 180~230℃;screw speed 320r/min
Injection temperature 190~210℃

Performance:

Tensile Strength/MPa70
Bending Elastic Modulus /GPa1.5
Heat Distortion Temperature/℃160
Impact/(J/m)40

Fiberglass reinforces PP

PP51%
LDPE5%
GF(5mm)40%
Tuttite dilate PP4%

Performance:

Tensile Strength/MPa97
Bending Elastic Modulus/GPa7.44
Impact/(J/m2)138.8

GF/LCP Composite Reinforced PP

PP70%
TLCP5%
GF30%

Performance:
Tensile Strength:51.3MPa;
Tensile Modulus: 1.59GPa.

Mica Reinforced PP

PP100
Silica Coupling0.25
Mica30

Performance:

Tensile Strength/MPa50
Bending Strength/MPa82
Hardness(R)106
Heat Distortion Temperature℃128
Deformation rate %1.2

Short Fiber Glass Reinforced PP

PP100
CaSt0.5
Activated Short Fiber Glass30
Anti-oxidant 10100.3
A-174 couplings0.1
Assistant Anti-oxidant DLTP0.5

Performance:

Tensile Strength MPa37.32
Elastic Modulus MPa252.19
Gap Impact Strength kJ/m28.15
Non-gap Impact Strength kJ/m229.55
Thermal Deformation ℃124.5

Silicon Fiber Reinforced PP

PP100
CaSt0.5
Silicon Fiber30
Anti-Oxidant 10100.3
KH-5500.5~1
Assistant Anti-oxidant DLTP0.3

Performance:

Tensile Strength/MPa28.54
Elastic Modulus /MPa201.92
Gap Impact Strength kJ/m28.32
Non-gap Impact Strength kJ/m232.10
Thermal Deformation /℃124.5

Composite Reinforced PP

PP100
Mica Powder15
Fiber Glass25
Silane Coupling0.5~1

Performance:

Tensile Strength MPa86.8
Bending Modulus MPa4200
Gap Impact Strength kJ/m27.1
Non-gap Impact Strength kJ/m220.1
Thermal Deformation ℃124.5

Fiber Glass Reinforce PVC

PVC100
Sulfuritol based Diopritne3
Coated Fiber Glass30
HSt0.5

Performance:

Bending Strength MPa113.7
Thermal Deformation ℃80.5
Cantilebal Impact Strength kJ/m219.1

Long Fiber Glass Reinforced PA6

1#2#
PA667.863.9
PP-g-MA4
Long Fiber Glass(10mm)32.232.1
Performance1#2#
Tensile Strength MPa208.4208.6
Bending Strength MPa269.5249.0
Impact Strength kJ/m263.468.7
Gap Impact Strength kJ/m229.032.3

Flame Retardant & Anti-static Reinforced PA6

PA640~55
Flame Retardant15~25
Tougher5~8
Anti-static agent5~8
Fiber Glass25~30

Anti-static Type Fiber Glass Reinforced PA6 Impeller

 Short GF Reinforced PA6(30% GF)94%
Short Carbon Fiber4.5%
Conductive Carbon Black0.5%

Flame Retardant Fiber Glass Reinforced PA6 Impeller

Short GF Reinforced PA6(30% GF)91%
Melamine4%
Sb2O35%

Transparent GF Reinforced PC

PC100
Polyteylene13.7
Chopped GF49
Silane Coupling0.33

Performance:

Young’s Modulus6.95GPa
Bending Modulus170MPa
Turbidity28%
Transmittance85%

Share:

More Blogs

Type of Twin Screw Extruder

Many people are confused about the type of twin screw extruder. Today’s article introduces three common twin-screw extruders, hoping to help readers better understand the

Type Of Plastic Extruder

Type of Plastic Extruder

Generally, for the type of plastic extruder, there are two kinds of plastic extruder that have to be mentioned. One is twin screw extruder and

Twin Screw Extruder Working Principle

Twin Screw Extruder Working Principle

The twin screw extruder working principle is mainly reflected in different screw shapes, and different shapes can show different production efficiency. in addition, there are